Preparing OLLA/PLLA Samples for Bone Tissue Culture
Pitkänen, Mika (2015)
2015
All rights reserved. This publication is copyrighted. You may download, display and print it for Your own personal use. Commercial use is prohibited.
Julkaisun pysyvä osoite on
https://urn.fi/URN:NBN:fi:amk-202401121346
https://urn.fi/URN:NBN:fi:amk-202401121346
Tiivistelmä
This thesis is a part of the research group in PIMA`s research about the usage of OLLA and PLLA in the bone tissue engineering. The objective of this thesis was to research the usage of OLLA/PLLA as scaffold material. The aim was to produce different composites of OLLA/PLLA and measure the chemical and physical properties of them.
The used method was solvent casting and salt leaching technique. In this technique porous structure is made with salt tube which is filled with polymers in liquid phase. After the polymers are settled in a tube and the tube is cooled down salt particles are leached out of the scaffold. By doing this only porous structure will remain. When producing OLLA the method from Valencia was used. In that method OLLA is formed by concentrating lactic acid.
Unfortunately the PLLA which was used had really high molecular weight. This caused a problem in solubility. Also the time was an issue, there was not enough time to do all the tests. And last but not least samples were ruined in later phase.
Still, it was possible to make porous scaffolds out of these polymers so further research is needed. Tämä opinnäyte työ tehtiin osana espanjalaista tutkimusryhmää. Työn aiheena oli selvittää OLLA/PLLA polymeerien käytön mahdollisuuksia luukudoksen kasvatuksessa käytettävän tukimateriaalin materiaalina. Tavoitteena oli valmistaa erilaisia seos suhteita kyseisistä polymeereistä ja mitata niiden fysikaalista ja kemikaalista kestävyyttä.
Menetelmänä käytettiin liuotin valua jossa huokoinen materiaali valetaan suolakiteiden päälle. Kun seos on jähmettynyt, suola poistetaan liuottimen avulla, jolloin jäljelle jää vain huokoinen tukiverkko. OLLA:n valmistuksessa käytettiin Valenciassa käytössä olevaa metodia, jossa LA:ta konsentroidaan.
Valitettavasti johtuen käytetystä polymeeristä, ajan vähyydestä ja epäonnesta varsinaisia mittaustuloksia ei saatu koskien tätä työtä. Käytetty polymeeri oli liian pitkäketjuinen ja näin ollen sen liukoisuus liuottimeen ei ollut kovin hyvä. Lisäksi näytteet olivat menneet pilalle myöhemmässä vaiheessa. Kuitenkin kyseisistä polymeereistä onnistui rakentaa tukiverkkoa. Tästä johtuen materiaalit vaativat lisää tutkimista ja kokeilua.
The used method was solvent casting and salt leaching technique. In this technique porous structure is made with salt tube which is filled with polymers in liquid phase. After the polymers are settled in a tube and the tube is cooled down salt particles are leached out of the scaffold. By doing this only porous structure will remain. When producing OLLA the method from Valencia was used. In that method OLLA is formed by concentrating lactic acid.
Unfortunately the PLLA which was used had really high molecular weight. This caused a problem in solubility. Also the time was an issue, there was not enough time to do all the tests. And last but not least samples were ruined in later phase.
Still, it was possible to make porous scaffolds out of these polymers so further research is needed.
Menetelmänä käytettiin liuotin valua jossa huokoinen materiaali valetaan suolakiteiden päälle. Kun seos on jähmettynyt, suola poistetaan liuottimen avulla, jolloin jäljelle jää vain huokoinen tukiverkko. OLLA:n valmistuksessa käytettiin Valenciassa käytössä olevaa metodia, jossa LA:ta konsentroidaan.
Valitettavasti johtuen käytetystä polymeeristä, ajan vähyydestä ja epäonnesta varsinaisia mittaustuloksia ei saatu koskien tätä työtä. Käytetty polymeeri oli liian pitkäketjuinen ja näin ollen sen liukoisuus liuottimeen ei ollut kovin hyvä. Lisäksi näytteet olivat menneet pilalle myöhemmässä vaiheessa. Kuitenkin kyseisistä polymeereistä onnistui rakentaa tukiverkkoa. Tästä johtuen materiaalit vaativat lisää tutkimista ja kokeilua.